01991nam a22001337a 4500999001700000100007400017245010000091260003000191300001100221500148900232700003601721942001101757952008901768  c55997d55994  aWagan, Riwan Hussain a10MCEM01aSupervisor - Prof.Dr. Abdullah Saand  aFlexural Strength Of Concrete Reinforced Beams By Using Steel Fiber Extracted from Waste Tyres   aNawabshsh:bQUEST,c2015.  a40p, :  a


Abstract 

The use of motor vehicles in Pakistan is increasing day-by-day because of which disposal of solid waste to the landfills of used tyres is a serious issue to be solved for Pakistan Environmental Protect Agency. Currently in this industry facing many challenges due to lack of support from government for the recycling and reuse of waste tyre by products, but manually a large quantity of high strength steel fibers (21 13 Mpa) are being extracted from waste tyres, the dominant use of this tyre-derived steel is a scrap steel to manufacture new iron or steel.

This research Work is focused on the use of steel fibers extracted from waste tyres and mixed in Concrete with different proportions to produce a concrete more strong than ordinary concrete. Different concrete specimens were casted and tested in universal testing machine to find flexural strength. The cement were replaced with steel fibers 0.5% 1%, 1 .5%, 2% and 2.5%. Result shows that the Concrete with inclusion of 1.5 % Waste Tyre Steel Fibers of 0.5 inch length gave maximum flexural strength (i.e. 0.675 MPa) which is 26.6%  more  than  that  of  plain concrete. Concrete with inclusion of 1.5% WTSF of 1 inch length gave maximum flexural strength (i.e. 0.69 MPa) was observed which is 28.3% more than that of plain  concrete

Generally, it can be concluded that Waste Tyre Steel Fibers concrete with inclusion of 1.5% of WTSF of 1 inch length is optimum in terms of flexural strength and workability.
  aDepartment Of Civil Engineering  cTHESIS  00104070aRESEARCHbRESEARCHd2016-11-23l0pMP/09-85r2016-11-23 00:00:00yTHESIS